First publ. in: Macromolecular Chemistry and Physics 204 (2003), F7-F8
Konstanzer Online-Publikations-System (KOPS) URL: http://www.ub.uni-konstanz.de/kops/volltexte/2008/6614/
URN: http://nbn-resolving.de/urn:nbn:de:bsz:352-opus-66148
Volltext
First publ. in: Macromolecular Chemistry and Physics 204 (2003), F7-F8
Konstanzer Online-Publikations-System (KOPS) URL: http://www.ub.uni-konstanz.de/kops/volltexte/2008/6614/
URN: http://nbn-resolving.de/urn:nbn:de:bsz:352-opus-66148
ÄHNLICHE DOKUMENTE
IR spectra of polymers
To investigate the effect of the organic phase in the catalytic emulsion polymerization of butadiene, the organic phase was omitted: the catalyst precursor was directly prepared in
TEM images of a silica/polyethylene composite dispersion using an octenyl-modified silica dispersed in toluene (Table 3,
In the presence of silica modified with octenylsilane 1 (Si1- 1 octen , diameter ∼ 110 nm), the nickel catalyst is able to polymerize ethylene, and a stable SiO 2
Summary: The preparation of aqueous dispersions of very small particles (size < 30 nm) of various polymers (polyethylenes, stereoregular 1,2-polybutadiene, and poly- alkenamers)
The different grey scales for different particles can be easily rationalized by different viewing angles: If the disc-like particles are nearly parallel to the electron beam,
Free radical emulsion polymerization of styrene or butyl acrylate in the presence of latices of linear, semicrystalline polyethylene prepared by catalytic emulsion polymeriza-
AFM images of PE/PS latex at different temperatures (top height mode, bottom phase